| Operation |
Endura |
Manganese |
Moly-Bond 500 |
Bending
Minimum bending radius
Rolling
Minimum Rolling
|
r ≥ 6 t
Perpendicular to Grain
d ≥ 40 t
|
r ≥ 1.5 t
Perpendicular to Grain
Not Recommended
|
r ≥ 9 t
Perpendicular to Grain
Not Recommended
|
Welding
Ct combined thickness
(Welding Energy: about 15 J/cm
|
No preheating
Up to Ct = 50 mm (2)
|
Never preheat
e < 20 kj/cm
|
Preheating for every thickness
|
Heat Cutting
(oxygen cutting, plasma
)
|
No preheating
Up to Ct = 40 mm (1.6”)
Cut underwater to reduce heat affected zone |
No preheating
Cut underwater to reduce heat affected zone |
Preheating for every thickness
Cut underwater to reduce heat affected zone |
Machining
Drilling, Milling
|
Tungsten Carbide – Tools or High speed steel with tip in tungsten carbide |
Tungsten Carbide – Tools or High speed steel with tip in tungsten carbide |
Tungsten Carbide – Tools or High speed steel with tip in tungsten carbide |
Impact Resistance
Toughness KCV
at 20C (-4 F)
|
Guarantee: > 40 J/sq cm
( > 23.6 ft – lb)
Typical Value: 55 J/ sq. cm
(32 ft – lbs) |
About 40 J/ sq. cm
(100 ft – lb)
C + 20C |
About 30 J/sq. cm.
(18 ft – lbs) |
Wear Resistance
(on an average)
|
About 8 times longer then mild steel |
About 10 times longer then mild steel with impact |
About 5 times longer then mild steel |