A) GENERAL INFORMATION
TITUS Moly-Bond 500 heat treated steel plate is intended for severe
wear applications requiring a high degree of abrasion resistance.
Originally developed for extreme wear applications including ballistics,
Titus Moly-Bond 500 combines a high carbon level with Titus's proven manganese,
moly-boron chemistry to produce a steel with up to fifteen times the wear resistance
of ordinary steel.
Titus A/R "MOLY- BOND" is heat treated to provide a
Brinell hardness range of 477 to 534 with a typical Brinell hardness of 514.
Abrasion resistance is typically 5:1 compared to mild steels.
B) CHEMICAL COMPOSITION
| GAUGE |
ELEMENT |
C(%) |
Mn(%) |
Si(%) |
S(%) |
P(%) |
Mo(%) |
B(%) |
| <
1.00IN(25MM) |
TYPICAL |
0.28% |
1.35% |
0.28% |
0.003% |
0.008% |
0.32% |
0.002% |
| MAX |
0.32% |
1.50% |
0.40% |
0.005% |
0.020% |
0.35% |
0.008% |
C) MECHANICAL CHARACTERISTICS
| MECHANICAL |
MINIMUM |
MAXIMUM |
TYPICAL |
| HARDNESS(BRINELL) |
477 |
534 |
514 |
| YIELD |
N/A |
N/A |
202 ksi (1390 Mpa) |
| TENSILE |
N/A |
N/A |
245 ksi (1690 Mpa) |
| ELONGATION IN 2 IN |
N/A |
N/A |
17% |
D) FIELDS OF APPLICATION
Examples:
Quarries, Construction - Earth Moving
Crushers
Screen
Bucket lip
Hoppers
Mines, Coal Mines
Excavators
Discharge
Conveyors
Cement Plants
Buckets
Crushers
Iron & Steel Industry
Guide
and shifting plates
Various casing
Hoppers
Transfer Trailers
Load
areas
Waste Disposal
N.B. - THIS LIST OF APPLICATIONS IS NOT
EXHAUSTIVE