Hardness
(Guaranteed values) |
HBW
280-330 (Approx. 30-35 HRC) |
| Impact properties (Guaranteed values) |
| Testing temperature °C 20-400°C |
Impact energy, Charpy-V, longitudinal direction;
min. ft. lbs. < 74-133 |
|
| Tensile Properties (Calculated values) |
Tensile strength approx. 130 - 142,000 PSI |
Milling
(Calculated values) |
At cutting speed of 300 m/mm, feed 0.15 mm, 10 min. effective cutting time using a Sandvik Coromil 200 and inserts GC 1025, we guarantee max 0.3 mm edge wear. |
Ultrasonic insp.
(Guaranteed values) |
Discontinuities giving echoes at least equivalent in amplitude to flat bottom hole 1.5 mm shall be reported according to SSAB Standard V6. |
| Etching properties (Guaranteed values) |
TOOLOX 33 fulfills the demands according to NADCA 207-97. |
Dimensions
(Preliminary) |
TOOLOX 33 is supplied in plate thickness 3/4” - 5 1/8”. |
| Delivery condition |
Quenched and tempered at min. 590°C |
| Heat treatment |
TOOLOX 33 is not intended for further heat treatment If TOOLOX 33 is subjected to any heat treatment above 590°C, after delivery from SSAB Oxelösund AB, no guarantees concerning the properties of the matrial will be given. |
| Testing |
Testing in accordance with EN 10 137-1, 10 137-2 and EN ISO 6506-1. Hardness measured on a milled surface, 0,5-2 mm below surface. |
| Tolerances |
According to EN 10 029
- Thickness tolerances to Class C.
- Flatness tolerances to Class N, steeltype L.
|
| Surface finish |
According to EN 10 163-2
- Surface requirements to Class B.
- Repair conditions to Subclass 3.
|